ENKAPSULASI EKSTRAK ETANOL DAUN SUNGKAI (Peronema canescens Jack) SEBAGAI INHIBITOR KOROSI PADA BAJA DALAM MEDIA ASAM SULFAT

Anggara, R. Restu Luky (2024) ENKAPSULASI EKSTRAK ETANOL DAUN SUNGKAI (Peronema canescens Jack) SEBAGAI INHIBITOR KOROSI PADA BAJA DALAM MEDIA ASAM SULFAT. S1 thesis, Universias Jambi.

	Text abstrak skripsi_R. Restu Luky Anggara.pdf Download (712kB)
	Text bab 1 skripsi_R. Restu Luky Anggara.pdf Download (745kB)
	Text bab 5 skripsi_R. Restu Luky Anggara.pdf Download (683kB)
	Text cover skripsi_R. Restu Luky Anggara.pdf Download (710kB)
	Text daftar pustaka skripsi_R. Restu Luky Anggara.pdf Download (752kB)
	Text skripsi_R. Restu Luky Anggara.pdf Restricted to Repository staff only Download (2MB)
	Text Halaman pengesahan skripsi_R. Restu Luky Anggara.pdf Download (4MB)

Abstract

Baja dalam industri digunakan sebagai material konstruksi karena kekuatan dan daya tahan baja. Baja rentan mengalami korosi jika berada di lingkungan yang korosif. Salah satu upaya dalam mengatasi permasalahan korosi yaitu dengan menggunakan inhibitor korosi. Enkapsulasi ekstrak sungkai memiliki efisiensi yang lebih baik dibandingkan inhibitor ekstrak sungkai. Metode yang digunakan dalam pembuatan enkapsulasi ekstrak etanol daun sungkai yaitu dengan metode homogenisasi. Efisiensi inhibisi baja ditentukan dengan metode kehilangan berat dengan variasi konsentrasi dan suhu perendaman baja. Dilakukan analisis Fourier Transform Infra Red (FTIR) untuk mengidentifikasi gugus fungsi yang terdapat dalam ekstrak dan enkapsulasi ekstrak etanol daun sungkai (Peronema canescens Jack). Dilakukan karakterisasi Scanning Electron Microscopy (SEM) untuk mengetahui morfologi permukaan baja sebelum dan setelah perendaman. Hasil penelitian menunjukkan laju korosi menurun seiring dengan dengan penambahan konsentrasi inhibitor enkapsulasi ekstrak etanol daun sungkai. Efisiensi inhibisi enkapsulasi ekstrak etanol daun sungkai konsentrasi 2,5g/L adalah 93,768% pada suhu 300C sedangkan ekstrak etanol daun sungkai efisiensi inhibisi sebesar 75,134%. Nilai efisiensi menurun pada suhu 40-600C akibat terjadinya desorpsi inhibitor pada permukaan baja. Mekanisme inhibitor enkapsulasi ekstrak etanol daun sungkai yaitu adsorpsi fisik dan mengacu pada isoterm Langmuir. Dari hasil parameter termodinamika, reaksi yang berlangsung secara spontan, eksoterm dan pada proses adsorpsi inhibitor terjadi secara teratur. Kata Kunci : Baja, Efisiensi, Ekstrak etanol daun sungkai (Peronema canescens Jack), Korosi, Enkapsulasi Steel in industry is used as a construction material because of the strength and durability of steel. Steel is susceptible to corrosion if it is in a corrosive environment. One effort to overcome corrosion problems is by using corrosion inhibitors. Encapsulation of sungkai ethanol extract has better efficiency than sungkai ethanol extract inhibitors. The method used to make encapsulation of ethanol extract sungkai leaf is the homogenizer method. The inhibition efficiency of steel is determined by the weight loss method with variations in concentration and immersion temperature of the steel. Fourier Transform Infra Red (FTIR) analysis was carried out to identify the functional groups contained in the extract and encapsulation of ethanol extract sungkai leaf (Peronema canescens Jack). Scanning Electron Microscopy (SEM) characterization was carried out to determine the morphology of the steel surface before and after immersion. The results showed that the corrosion rate decreased along with the addition of the encapsulated inhibitor concentration of ethanol extract sungkai leaf. The encapsulation inhibition efficiency of ethanol extract sungkai leaf with a concentration of 2.5g/L was 93.768% at a temperature of 300C while the inhibition efficiency of ethanol extract sungkai leaf was 75.134%. The efficiency value decreases at temperatures of 40-600C due to inhibitor desorption on the steel surface. The inhibitor mechanism for encapsulation of ethanol extract sungkai leaf is physical adsorption and refers to the Langmuir isotherm. From the results of the thermodynamic parameters, reactions that take place spontaneously, are exothermic and in the inhibitor adsorption process occur regularly. Keywords: Steel, Efficiency, Ethanol Extract Sungkai Leaf (Peronema canescens Jack), Corrosion, Encapsulation

Type:	Thesis (S1)
Subjects:	L Education > L Education (General)
Divisions:	Fakultas Sains dan Teknologi > Kimia
Depositing User:	ANGGARA
Date Deposited:	13 Jan 2025 07:27
Last Modified:	13 Jan 2025 07:27
URI:	https://repository.unja.ac.id/id/eprint/74347

Actions (login required)

View Item